ASME SA543 Type B Class 1 Steel Plate | SA543 Type B Cl.1 QT Ni-Cr-Mo Vessel Plate

ASME SA543 Type B Class 1, also written ASME SA543 TYPE B CL.1, is quenched-and-tempered nickel-chromium-molybdenum alloy plate under ASME SA-543/SA-543M. The specification is identical with ASTM A543/A543M. It covers plates intended for welded pressure vessels and other pressure equipment, normally considered for construction involving plate thicknesses of 50 mm or greater. Type B and Type C are the only Types in the current book. Type A is not a live listing. Each Type is available as Class 1, Class 2 and Class 3. Class 1 is 585 MPa yield and 725–860 MPa tensile. SHH STEEL is the supplier, exporter, distributor and stockist of this Type and Class. Plate is produced to ASME SA-543/SA-543M.

Buyers write ASME SA543 Type B Class 1, ASME SA543 TYPE B CL.1, SA543 Type B Class 1, SA543 Type B Cl.1, SA543B CL1, SA-543 Type B Class 1, SA 543 Type B Cl 1 and A543 Type B Class 1. A purchase order that only says “SA543 Type B” is incomplete. A purchase order that says “SA543 Grade B Class 1” is mixing Type language with Grade language. This book uses Type + Class, the same naming idea as SA542, not the Grade A/B/C idea used on SA516 Gr.70.

This page is not Type C. Type C nickel heat is 2.00–3.50% and carbon heat is 0.18% max. Type B nickel heat is 2.25–4.00% and carbon heat is 0.20% max. This page is not Class 2 (690 MPa yield, 795–930 MPa tensile) and not Class 3 (485 MPa yield, 620–795 MPa tensile). It is not SA387 Gr.22 Cl.2. It is not SA542 Type B Class 1, which is 2.25Cr-1Mo QT without this nickel band. It is not SA517 Gr.B. It is not SA533 Type B Cl.1. Minimum thickness in the specification is 5 mm. Maximum thickness is limited only by the ability of the chemistry to meet Class 1 after quench and temper. In practice, SA543 is asked for thick reactor shells, not for thin tank floors.

The specification warns that these alloy plates in the as-rolled condition are sensitive to cracking during flame cutting, transit and handling. They should be shipped as-rolled only by mutual agreement. The product on this page is quenched and tempered. Dual marking SA543 / A543 Type B Class 1 is available from SHH STEEL as mill supplier. Certificates can be EN 10204 3.1 or 3.2. Company scope: China steel Mill Agent-SHH STEEL.

This plate sits in pressure vessel steel plates and next to the ASME SA387 family, not as a substitute. It does not sit with carbon steel plates or ASTM A36 steel plate.

SA-20 still governs marking, testing location, retests, repair rules and supplementary requirements unless the product specification overrides them. Vacuum carbon-deoxidized steel under S17 is sometimes added on thick Ni-Cr-Mo heats.

ASME SA543 Type B Class 1 / ASME SA543 TYPE B CL.1 uses Type B chemistry. Class only changes strength. Nickel, chromium and molybdenum are the alloy idea. Manganese is held low compared with ordinary C-Mn vessel plate.

Heat Analysis and Product Analysis — ASME SA543 Type B (typical Table 1 limits)

Type C carbon heat is 0.18% max and nickel heat is 2.00–3.50%. Do not ship Type C as Type B because both are Ni-Cr-Mo. Do not treat this chemistry as SA387 Gr.11 Cl.2 or SA387 Gr.12 Cl.2. Those books are Cr-Mo without this nickel band.

SHH STEEL reports heat analysis on every certificate, including Ni, Cr and Mo, and product analysis when SA-20 requires it. If the vessel specification tightens phosphorus or sulfur below the table, write that on the order. Do not assume a hydroprocessing residual package.

Class 1 is the mid-high line in this book. Class 2 is stronger. Class 3 is lower tensile with more elongation.

Tensile Requirements — ASME SA543 Type B Class 1

Class 2 is 690 MPa yield and 795–930 MPa tensile, still 14% elongation. Class 3 is 485 MPa yield, 620–795 MPa tensile and 16% elongation. Do not stamp Class 3 as Class 1 because a coupon came in high. Do not quote Class 2 numbers on a thickness the mill cannot quench through.

Density is 7.85 g/cm³. Notch toughness is commonly added on reactor plate. Write the temperature, energy, location and orientation. Simulated PWHT is common because thick Ni-Cr-Mo vessels see long furnace cycles after welding. Through-thickness properties and ultrasonic quality matter more on this grade than on thin SA285 Gr.C.

Do not treat 585 MPa yield as permission to substitute A516 Grade 70, SA533 Type C Cl.1 or high strength low alloy plates. Those families do not carry Type B nickel.

SA299 Gr.A, SA225 Gr.C, SA455 steel plate and SA203 Gr.A are also vessel plates. None of them is ASME SA543 TYPE B CL.1.

ASME SA543 Type B Class 1 / ASME SA543 TYPE B CL.1 is selected when the vessel wants quenched-and-tempered Ni-Cr-Mo at the Class 1 strength line, usually in heavier thickness. Typical equipment is large welded reactors, high-pressure shells and other pressure equipment written to SA-543 Type B Class 1. The specification itself notes that these compositions are normally considered for construction involving plate 50 mm or greater. Allowable stress comes from ASME Section II Part D after the Code lists this Type and Class.

SHH STEEL supplies this plate as exporter and stockist. It is not nickel low-temp plate like SA203 Gr.D or SA203 Gr.E. Those grades use nickel for toughness at low temperature, not this Ni-Cr-Mo QT combination. It is not layered QT carbon like SA724. It is not SA302 Gr.B. Stainless inquiries belong on ASME SA240 or ASTM A240.

Do not form this plate as if it were as-rolled SA285 Gr.A. Quench-and-temper properties are the product. Flame cutting of as-rolled mother plate is a cracking risk. A later PWHT cycle has to be planned and, when required, simulated on coupons. Residual stress in heavy welded joints is a real shop issue on this grade. The fabricator owns preheat, hydrogen control and PWHT, not the mill certificate alone.

SA543 Type B Cl.1 is killed Ni-Cr-Mo at Class 1 strength. Welding is Code welding.

Qualify procedures to ASME Section IX. Use consumables written for QT Ni-Cr-Mo at 725–860 MPa tensile, not a plain carbon procedure and not an unreviewed SA387 Gr.22 Cl.2 procedure. Nickel, chromium and molybdenum all belong in the WPS review. Hydrogen control, preheat, interpass and PWHT follow the qualified procedure and the vessel specification. Thick joints without a planned heat cycle can leave residual stress that later shows up as cracking in service.

Do not copy a SA387 Gr.12 Cl.2 procedure onto Type B Class 1 without review. The fabricator owns the WPS. SHH STEEL as supplier can share mill heat data, cooling practice and simulated PWHT coupon results for that review.

Plates shall be quenched and tempered. Austenitize, quench in a suitable liquid medium, then temper. Soak times follow the mill procedure and the thickness. The specification does not use the SA542 Type A/B/C Class 1 temper floor of 565 °C as a copy-paste rule. Print the actual austenitizing and tempering temperatures on the certificate when the mill record carries them.

As-rolled shipment is a special agreement, not the default. The specification states that as-rolled plates of this alloy are sensitive to cracking during flame cutting, transit and handling. SHH STEEL as mill exporter treats QT as the delivery condition unless the purchase order and the mill both accept as-rolled with handling limits.

If the vessel will see a long PWHT, test coupons shall follow a simulated cycle. This is not the SA832 N+T route and not the SA537 Cl.1 heat-treated carbon route. Do not apply a carbon-plate normalize cycle and call the plate SA543 Type B Class 1.

Usual delivery from SHH STEEL as supplier and distributor is quenched-and-tempered ASME SA543 Type B Class 1 / ASME SA543 TYPE B CL.1 plate.

The certificate lists ASME SA543 Type B Class 1 and, when dual certified, ASTM A543 Type B Class 1; heat number; heat analysis including Ni, Cr and Mo; product analysis when ordered; tensile results to the Class 1 table; QT statement; impact and simulated PWHT when ordered. Certificates may be EN 10204 3.1 or EN 10204 3.2.

Surface is mill scale unless the order names shot blast, paint or machine allowance. Cutting, beveling and rolling sketches belong on the purchase order. Do not assume stock lengths on a 100 mm reactor plate.

Usual supply range from SHH STEEL for SA543 Type B Cl.1 QT Ni-Cr-Mo vessel plate:

• Thickness: commonly 20 mm – 150 mm, minimum 5 mm. The specification is written with heavy plate in mind. Confirm the mill can hold 585 MPa yield through the ordered thickness
• Width: 1500 mm – 4000 mm
• Length: 3000 mm – 12000 mm
• Cut-to-length shells, heads and nest sizes inside those limits

Structural sizes belong on EN 10025-2 or JIS G3106. Weathering plate belongs on EN 10025-5 or Corten A/B. Fine-grain structural belongs on EN 10025-3 or EN 10025-4. QT structural belongs on EN 10025-6.

Dimensional limits follow ASME SA-20. Thickness, width, length, flatness and camber are vessel-plate tolerances, not structural-plate tolerances from ASTM A36/A36M. UT to A435 / A577 / A578 is commonly added on reactor plate. Write the UT level on the order. Do not assume Class C scanning if the vessel specification names a tighter level.

Crown, waviness and residual stress after quench matter on wide thick plate. If the shop will roll a tight diameter, say so before rolling. Repair welding of surface defects follows SA-20 rules unless the order forbids repair.

Most export ASME SA543 Type B Class 1 / ASME SA543 TYPE B CL.1 orders add extras. SHH STEEL as supplier does not assume them.

Charpy details. Temperature, energy, location and orientation. Thick Ni-Cr-Mo plate often needs more than a single default temperature.

Simulated PWHT. Same-heat coupons follow the vessel cycle, including hold time at the PWHT temperature.

NDE. UT to A435 / A577 / A578. Magnetic particle on cut edges when specified.

Vacuum carbon deoxidation (S17). Sometimes specified on heavy heats.

Hydrogen-service extras. When the vessel specification names them.

Through-thickness / Z-direction testing. When the drawing names it.

Third-party. EN 10204 3.2.

These names are project-comparison grades. They are not automatic substitutes.

DIN 17100, ASTM A516, ASME SA515 and ASTM A285 are not SA543 Type B Class 1.

Ship plate inquiries belong on shipbuilding steel plates or BV Rules. Weathering inquiries belong on weathering steel plates. Stainless inquiries belong on stainless steel products, JIS G4305 or AISI stainless.

Other vessel comparisons: SA203 Gr.B, SA302 Gr.C, A516 Grade 70, SA533 Type C Cl.2, SA517 Gr.P.

SHH STEEL is the supplier, exporter, distributor and stockist of ASME SA-543/SA-543M plate. On ASME SA543 Type B Class 1 / ASME SA543 TYPE B CL.1 that means mill pricing, dual SA543/A543 marking, Type B chemistry with Ni-Cr-Mo reported, recorded quench and temper, tensile results at 585 MPa yield and 725–860 MPa tensile, 3.1 as standard and 3.2 when specified.

We keep Type and Class on the order. Type B is not Type C. Class 1 is not Class 2 and is not Class 3. SA543 is not SA542. SA543 is not SA387 Gr.22 Cl.2. SA543 is not SA516 Gr.55. SA543 Type B Cl.1 is not SA533 Type C Cl.1. If the drawing names Class 2, we will not ship Class 1 and call it close. If the shop wants as-rolled delivery on this alloy, we will say the specification treats that as a cracking risk.

Company scope: China steel Mill Agent-SHH STEEL.

ASME SA543 Type B Class 1 Steel Plate, also searched as ASME SA543 TYPE B CL.1, is quenched-and-tempered Ni-Cr-Mo plate under ASME SA-543/SA-543M, with Type B nickel and Class 1 strength. Whether the inquiry says ASME SA543 Type B Class 1, ASME SA543 TYPE B CL.1, SA543 Type B Cl.1 or SA543B CL1, SHH STEEL as supplier, exporter, distributor and stockist supplies plate with Type B chemistry, recorded QT delivery, 585 MPa yield, and EN 10204 3.1 or 3.2 certification.

SHH STEEL is the China mill vendor of ASME SA543 Type B Class 1 / ASME SA543 TYPE B CL.1 QT Ni-Cr-Mo Vessel Plate for ASME Section VIII work that actually names this Type and Class.

Contact SHH STEEL for mill rolling, stock inquiry, dual SA543/A543 marking, simulated PWHT testing, 3.2 inspection or a quotation.

ASME SA543 Type B Class 1 Steel Plate, ASME SA543 TYPE B CL.1, SA543 Type B Cl.1, SA543B CL1, SA-543 Type B Class 1, QT Ni-Cr-Mo vessel plate, SHH STEEL supplier exporter distributor stockist