GB/T 4237 022Cr25Ni22Mo2N S31053 Stainless Steel Plate Supplier
022Cr25Ni22Mo2N S31053 plate at a glance
022Cr25Ni22Mo2N is 310MoLN (EN 1.4466), a fully austenitic 25Cr-22Ni-2Mo grade with nitrogen and very low carbon (≤0.020%). Annex B lists it for urea synthesis towers, strippers and carbamate condensers, where it must stay non-magnetic and resist strongly oxidizing carbamate solution.
Reading the designation: ‘022’ gives the carbon level (C ≤0.020% in GB/T 4237), followed by Cr25 = about 25% chromium; Ni22 = about 22% nickel; Mo2 = about 2% molybdenum; N = nitrogen added. S31053 is the unified numeric code (ISC) used in GB/T 4237-2015.
SHH STEEL produces and exports austenitic stainless plate from China, works as a sales agent for leading stainless mills, and runs its own processing warehouse for cutting and surface finishing. 022Cr25Ni22Mo2N is part of our GB/T 4237 stainless plate range; for comparison, see our ASTM A240 Type 310S page.
How 022Cr25Ni22Mo2N performs in corrosive service
Super austenitic grades are chosen when 316L and 317L pit or crevice-corrode: seawater, bleach plant filtrates, hot brines, sulfuric and phosphoric acids with chloride.
PREN of 022Cr25Ni22Mo2N from the GB/T 4237 limits: 30.7 – 33.9. PREN is a ranking tool for pitting in chlorides, not a guarantee; temperature, crevices, deposits and weld finish matter as much.
Intergranular corrosion testing is not compulsory for this grade in GB/T 4237-2015; when required, the method (GB/T 4334, ASTM A262 or A923 for duplex) and acceptance are agreed in the order.
For critical service, order ASTM G48 Method A (ferric chloride pitting) or Method C/E (critical pitting temperature) tests on the plate heat. We arrange them at the mill or an independent laboratory.
If service is harsher than 022Cr25Ni22Mo2N can handle, the next step up in this batch is GB/T 4237 022Cr23Ni5Mo3N S22053.
022Cr25Ni22Mo2N chemical composition (heat analysis)
| Element | 022Cr25Ni22Mo2N heat analysis, % (Table 15) | Why it matters |
|---|---|---|
| C | ≤ 0.020 | Carbon. Low values protect welds from carbide precipitation; higher values add hot strength or hardenability. |
| Si | ≤ 0.50 | Silicon. Deoxidizer; in heat-resistant grades it builds a protective scale. |
| Mn | ≤ 2.00 | Manganese. Deoxidizer; in Mn-bearing grades it replaces nickel and keeps nitrogen in solution. |
| P | ≤ 0.030 | Phosphorus. Impurity, kept low for toughness and weld cracking resistance. |
| S | ≤ 0.010 | Sulfur. Impurity; low sulfur improves pitting resistance, hot workability and polishability. |
| Cr | 24.00 – 26.00 | Chromium. Forms the passive film; the main driver of corrosion and oxidation resistance. |
| Ni | 20.50 – 23.50 | Nickel. Stabilizes austenite, improves toughness and resistance to reducing acids. |
| Mo | 1.60 – 2.60 | Molybdenum. Raises pitting and crevice resistance in chlorides (×3.3 in PREN). |
| N | 0.09 – 0.15 | Nitrogen. Strengthens, stabilizes austenite and adds pitting resistance (×16 in PREN). |
| PREN (Cr + 3.3Mo + 16N) | 30.7 – 33.9 (minimum – mid-range) | Calculated from the limits above, not a requirement of GB/T 4237 |
Values are maximum unless a range is given. The mill reports the ladle (heat) analysis on the certificate; this is the figure to compare with Table 15.
Product (check) analysis tolerances
A check analysis drilled from the finished plate may differ slightly from the heat analysis. GB/T 4237 refers to GB/T 222 for the permitted deviations; the table applies them to the 022Cr25Ni22Mo2N limits. Deviations apply to one side of a range only, never to both sides in the same heat.
| Element | Heat analysis limit (%) | Permitted deviation | Product analysis limit (%) |
|---|---|---|---|
| C | ≤ 0.020 | +0.005 | ≤ 0.025 |
| Si | ≤ 0.50 | ±0.05 | ≤ 0.55 |
| Mn | ≤ 2.00 | ±0.04 | ≤ 2.04 |
| P | ≤ 0.030 | +0.005 | ≤ 0.035 |
| S | ≤ 0.010 | +0.005 | ≤ 0.015 |
| Cr | 24.00 – 26.00 | ±0.25 | 23.75 – 26.25 |
| Ni | 20.50 – 23.50 | ±0.20 | 20.30 – 23.70 |
| Mo | 1.60 – 2.60 | ±0.05 (min) / ±0.10 (max) | 1.55 – 2.70 |
| N | 0.09 – 0.15 | ±0.01 | 0.08 – 0.16 |
Where the table says ‘by agreement’, the deviation is not tabulated for that content level and should be agreed in the contract, usually by reference to ASTM A480 Table A1.1.
Mechanical properties at room temperature
| Property | 022Cr25Ni22Mo2N (Table 20) |
|---|---|
| Proof strength Rp0.2, MPa | ≥ 270 |
| Tensile strength Rm, MPa | ≥ 580 |
| Elongation A, % | ≥ 25 |
| Hardness HBW | ≤ 217 |
| Hardness HRB | ≤ 95 |
| Hardness HV | ≤ 220 |
Values apply to plate in the delivery heat-treated condition, tested transversely per GB/T 228.1. Hardness is checked by one method chosen by the mill.
Cross-reference to other standards
| Standard system | Equivalent / closest grade |
|---|---|
| China GB/T 4237-2015 | 022Cr25Ni22Mo2N (S31053) |
| ASTM A240/A240M | 310MoLN / S31050 |
| EN 10088-2 | X1CrNiMoN25-22-2 / 1.4466 |
| JIS G4304 (hot rolled) | — |
| Common name | 310MoLN (urea grade) |
Equivalent grades are close in chemistry and properties but are never identical: limits on carbon, nitrogen and residual elements differ. For dual or multiple certification the heat must meet every standard named on the order, and we confirm that from the heat chemistry before quotation.
Related pages: ASTM A240 Type 310S, AISI 310S. See also our ASTM A240/A240M and JIS G4305 plate lists.
Where this grade sits on the super austenitic ladder
The high-alloy austenitics of GB/T 4237 step up in molybdenum and nitrogen. Pitting resistance follows PREN closely; nickel mainly helps in acids and against phase precipitation.
| Grade | Mo, % | N, % | PREN min |
|---|---|---|---|
| GB/T 4237 015Cr21Ni26Mo5Cu2 S31782 | 4.00 – 5.00 | ≤ 0.10 | 32.2 |
| GB/T 4237 015Cr20Ni18Mo6CuN S31252 | 6.00 – 6.50 | 0.18 – 0.25 | 42.2 |
| GB/T 4237 015Cr20Ni25Mo7CuN S38926 | 6.00 – 7.00 | 0.15 – 0.25 | 41.2 |
| GB/T 4237 022Cr21Ni25Mo7N S38367 | 6.00 – 7.00 | 0.18 – 0.25 | 42.7 |
| GB/T 4237 022Cr24Ni17Mo5Mn6NbN S34553 | 4.00 – 5.00 | 0.40 – 0.60 | 42.6 |
| GB/T 4237 015Cr24Ni22Mo8Mn3CuN S32652 | 7.00 – 8.00 | 0.45 – 0.55 | 54.3 |
022Cr25Ni22Mo2N: 310MoLN.
Fabrication guidance
Weld super austenitic plate with over-alloyed nickel-base filler (ERNiCrMo-3, ERNiCrMo-10 or ERNiCrMo-13 class). Matching filler leaves Mo-depleted dendrite cores that pit before the parent metal.
Heat input ≤1.5 kJ/mm, interpass ≤100 °C, full argon back purge, and pickling of the whole weld zone. Avoid autogenous (no-filler) GTAW on wetted surfaces.
Cutting: we cut 022Cr25Ni22Mo2N by plasma (up to about 150 mm), laser (thin plate) or waterjet, and remove the heat-affected edge by machining where the drawing requires it.
Annealing / solution treatment
Recommended heat treatment for 022Cr25Ni22Mo2N (GB/T 4237-2015 Annex C): ≥ 1 040 °C, water quench or other rapid cooling.
Super austenitic plate must be quenched fast from the solution temperature to keep sigma and chi phases out of the structure. Hot-formed heads are re-annealed at the same temperature.
GB/T 4237 022Cr25Ni22Mo2N specification details
| Item | GB/T 4237-2015 requirement / SHH STEEL supply |
|---|---|
| Standard | GB/T 4237-2015 Hot rolled stainless steel plate, sheet and strip (current edition, replaces GB/T 4237-2007) |
| Grade / unified code | 022Cr25Ni22Mo2N / S31053 |
| Steel class | Austenitic |
| Chemical composition | Table 15 (heat analysis); product analysis per GB/T 222 |
| Mechanical properties | Table 20 |
| Product forms | Hot-rolled thick plate (3.0 – 200 mm in the standard), hot-rolled wide strip and cut plate (2.0 – 25.4 mm) |
| Our usual thickness range | 3 – 50 mm |
| Delivery condition | ≥ 1 040 °C, water quench or other rapid cooling |
| Surface | Hot rolled, heat treated, pickled (No.1 / 1D) as standard; ground or polished by agreement |
| Density | 8.0 g/cm³ |
| Certificate | EN 10204 3.1 mill certificate; 3.2 with third-party inspection on request |
Sister grades on the same standard are listed under GB/T 4237; cold-rolled sheet of the same chemistry is ordered to GB/T 3280, and all our plate lines sit in stainless steel sheets and plates.
Applications of 022Cr25Ni22Mo2N plate
Severe-service applications:
- Urea synthesis reactors, HP strippers and carbamate condensers
- Nitric acid and ammonium nitrate equipment
- Lining and cladding for high-pressure urea vessels
- Chemical equipment needing non-magnetic, ferrite-free metal
Buyers specifying 022Cr25Ni22Mo2N for these jobs often compare it with GB/T 4237 06Cr25Ni20 S31008 and GB/T 4237 022Cr23Ni5Mo3N S22053; the comparison table on this page shows the differences.
International grade pages for the alternatives mentioned above: AISI 316LN, ASTM A240 Type 904L, ASTM A240 Type 2205.
022Cr25Ni22Mo2N compared with related grades
The table compares 022Cr25Ni22Mo2N with the grades buyers most often weigh it against. Strength values are GB/T 4237-2015 minimums; PREN is calculated from the minimum chemistry.
| Grade (GB/T 4237) | Key chemistry, % | PREN min | Rp0.2 min, MPa | Rm min, MPa |
|---|---|---|---|---|
| 022Cr25Ni22Mo2N S31053 | C ≤ 0.020, Cr 24.00 – 26.00, Ni 20.50 – 23.50, Mo 1.60 – 2.60, N 0.09 – 0.15 | 30.7 | 270 | 580 |
| GB/T 4237 06Cr25Ni20 S31008 | C ≤ 0.08, Cr 24.00 – 26.00, Ni 19.00 – 22.00 | 24.0 | 205 | 515 |
| GB/T 4237 022Cr17Ni12Mo2N S31653 | C ≤ 0.030, Cr 16.00 – 18.00, Ni 10.00 – 14.00, Mo 2.00 – 3.00, N 0.10 – 0.16 | 24.2 | 205 | 515 |
| GB/T 4237 015Cr21Ni26Mo5Cu2 S31782 | C ≤ 0.020, Cr 19.00 – 23.00, Ni 23.00 – 28.00, Mo 4.00 – 5.00, N ≤ 0.10, Cu 1.00 – 2.00 | 32.2 | 220 | 490 |
| GB/T 4237 022Cr23Ni5Mo3N S22053 | C ≤ 0.030, Cr 22.00 – 23.00, Ni 4.50 – 6.50, Mo 3.00 – 3.50, N 0.14 – 0.20 | 34.1 | 450 | 655 |
Urea licensors (Stamicarbon, Saipem/Snamprogetti, Toyo) add their own limits: ferrite ≤0.5%, selective Huey test (65% boiling nitric acid) rates, extra Cr/Ni/Mo windows and 100% UT. Send us the licensor spec; GB/T 4237 compliance alone is not sufficient.
Surface options and cut-to-size service
| Finish | Description | Availability for this grade |
|---|---|---|
| No.1 / 1D | Hot rolled, heat treated, pickled; the GB/T 4237 standard surface | Standard |
| Shot-blasted + pickled | Uniform matte for welded structures | On request |
| Ground | Ground surface for defect removal or UT | On request |
| 2B / BA | Cold-rolled finishes (ordered as GB/T 3280 sheet, not hot-rolled plate) | Sheet only |
Our warehouse cuts plate to size (plasma, laser, waterjet, saw), bevels weld edges, polishes and applies PVC protective film. Processed plate ships with the original mill heat number marked. Ask for cut pieces of other stainless steel products at the same time to consolidate freight.
Sizes, tolerances and weight
| Dimension | Typical supply |
|---|---|
| Thickness | 3 – 50 mm |
| Width | 1 000 / 1 219 / 1 250 / 1 500 / 1 800 / 2 000 mm; wider by mill order |
| Length | 2 000 / 2 438 / 3 000 / 6 000 mm or cut to size |
| Flatness | Per GB/T 4237; ≤15 mm per metre for plate up to 25 mm unless agreed tighter |
| Thickness tolerance | Per the GB/T 4237 dimensional tolerance tables (normal or higher accuracy as ordered) |
| Edge | Mill edge or cut edge |
Weight: plate mass in kg/m² = thickness (mm) × density (8.0 g/cm³). A 10 mm 022Cr25Ni22Mo2N plate weighs about 80.0 kg/m²; a 1 500 × 6 000 × 10 mm plate about 720 kg.
Testing and certification
- Heat chemical analysis on every heat; product analysis by agreement
- Tensile test (Rp0.2, Rm, A) per batch
- Hardness test
- ASTM G48 pitting test when specified
- Ultrasonic testing (NB/T 47013.3 or ASTM A578) when specified
- Positive material identification (PMI) on every plate leaving our warehouse
- Visual and dimensional inspection; third-party inspection (SGS, BV, TÜV, Intertek) at the buyer’s request
Certificates follow EN 10204 3.1 as standard. Where plate is also certified to ASME SA240 or ASTM A240, both standards are shown on one certificate.
Where our plate comes from
022Cr25Ni22Mo2N is produced by a small number of Chinese mills with the melting and heat treatment capability for it. We place mill orders for it through the producers we represent and do not usually hold it in stock. Expect about 45–90 days, with minimum quantities per thickness; we can combine small quantities into one rolling where the mill allows.
Every plate is traceable to its heat number, and copies of the mill certificates stay on file for repeat orders and audits. The same mills also supply our ASTM A240, ASME SA240, JIS G4305 and AISI plate ranges, so mixed-standard orders can ship together.
What to put on a 022Cr25Ni22Mo2N purchase order
- Standard and edition: GB/T 4237-2015
- Grade and code: 022Cr25Ni22Mo2N (S31053); add the equivalent if dual certification is needed
- Thickness × width × length, quantity in pieces or tonnes
- Thickness tolerance class and flatness if tighter than standard
- Surface finish and protective film
- Tests beyond the standard (IGC, UT, impact, ferrite, PMI, grain size)
- Certificate type (EN 10204 3.1 / 3.2) and inspection body
- Marking, packing (wooden cases, steel pallets) and delivery terms
Send the list to SHH STEEL and we return a quotation with mill, lead time and stock options. Other grades from the same standard can be combined in one shipment; browse GB/T 4237 plate grades.
FAQ
- What is 022Cr25Ni22Mo2N used for?
- 022Cr25Ni22Mo2N (S31053, 310MoLN, EN 1.4466) is used mainly in urea plants: synthesis towers, high-pressure strippers and carbamate condensers. GB/T 4237-2015 requires 270 MPa proof strength, 580 MPa tensile and 25% elongation; urea service adds ferrite and Huey test limits.
- What is the chemical composition of 022Cr25Ni22Mo2N?
- Under GB/T 4237-2015 Table 15, 022Cr25Ni22Mo2N (S31053) has C ≤ 0.020, Cr 24.00 – 26.00, Ni 20.50 – 23.50, Mo 1.60 – 2.60, N 0.09 – 0.15. Phosphorus is limited to ≤0.030% and sulfur to ≤0.010%.
- What is the ASTM equivalent of 022Cr25Ni22Mo2N?
- The closest equivalents of 022Cr25Ni22Mo2N (S31053) are 310MoLN / S31050 in ASTM, X1CrNiMoN25-22-2 / 1.4466 in EN (common name: 310MoLN (urea grade)). Chemistry limits differ slightly, so dual certification depends on the actual heat.
- What are the mechanical properties of 022Cr25Ni22Mo2N plate?
- GB/T 4237-2015 Table 20 requires for 022Cr25Ni22Mo2N: proof strength Rp0.2 ≥270 MPa, tensile strength ≥580 MPa and elongation ≥25%, hardness ≤217 HBW. Values apply to plate in the delivery heat-treated condition.
- Is 022Cr25Ni22Mo2N stainless steel magnetic?
- Not in the annealed condition. 022Cr25Ni22Mo2N is austenitic, so annealed plate is essentially non-magnetic; cold work can induce slight magnetism, mostly at cut and bent edges.
- What thickness of 022Cr25Ni22Mo2N plate can you supply?
- Under GB/T 4237 we supply 022Cr25Ni22Mo2N hot-rolled plate in 3 – 50 mm, widths up to 2 000 mm (wider by mill order), cut to size in our warehouse. Thinner material is cold-rolled sheet to GB/T 3280.
Conclusion
GB/T 4237 022Cr25Ni22Mo2N (S31053) is a super austenitic / high-alloy austenitic plate grade, known internationally as 310MoLN. It is defined by Table 15 chemistry (C ≤ 0.020, Cr 24.00 – 26.00, Ni 20.50 – 23.50, Mo 1.60 – 2.60, N 0.09 – 0.15) and Table 20 properties of at least 270 MPa proof strength and 580 MPa tensile strength. Typical uses include urea synthesis reactors, hp strippers and carbamate condensers, nitric acid and ammonium nitrate equipment and lining and cladding for high-pressure urea vessels. Urea licensors (Stamicarbon, Saipem/Snamprogetti, Toyo) add their own limits: ferrite ≤0.5%, selective Huey test (65% boiling nitric acid) rates, extra Cr/Ni/Mo windows and 100% UT.
Before ordering, state the standard edition, the grade name with its code, and any extra tests, so that the mill certificate matches your design documents. SHH STEEL supplies 022Cr25Ni22Mo2N plate by mill order through the producers we represent, cut to size and finished in our own warehouse, with EN 10204 3.1 certificates. For related grades see GB/T 4237 06Cr25Ni20 S31008 and GB/T 4237 022Cr17Ni12Mo2N S31653, our GB/T 4237 category and the ASTM A240 Type 310S page. Send your sizes and quantities for a quotation.