GB/T 4237 06Cr17Ni12Mo2 S31608 Stainless Steel Plate Supplier
What is GB/T 4237 06Cr17Ni12Mo2 (S31608) stainless steel plate?
06Cr17Ni12Mo2 is China’s 316: the 18-8 base with 2.00–3.00% molybdenum and nickel raised to 10.00–14.00%. Molybdenum is what lets it handle seawater spray, chlorides and many organic acids that pit 304.
How to read the name: under GB/T 20878 the leading ’06’ is the carbon code (here C ≤0.08%), then Cr17 = about 17% chromium; Ni12 = about 12% nickel; Mo2 = about 2% molybdenum. S31608 is the unified numeric code (ISC) used in GB/T 4237-2015. Older drawings and Chinese buyers may still write the pre-2007 name 0Cr17Ni12Mo2.
SHH STEEL produces and exports austenitic stainless plate from China, works as a sales agent for leading stainless mills, and runs its own processing warehouse for cutting and surface finishing. 06Cr17Ni12Mo2 is part of our GB/T 4237 stainless plate range; for comparison, see our ASTM A240 Type 316 page.
Heat analysis limits for 06Cr17Ni12Mo2
| Element | 06Cr17Ni12Mo2 heat analysis, % (Table 15) | Why it matters |
|---|---|---|
| C | ≤ 0.08 | Carbon. Low values protect welds from carbide precipitation; higher values add hot strength or hardenability. |
| Si | ≤ 0.75 | Silicon. Deoxidizer; in heat-resistant grades it builds a protective scale. |
| Mn | ≤ 2.00 | Manganese. Deoxidizer; in Mn-bearing grades it replaces nickel and keeps nitrogen in solution. |
| P | ≤ 0.045 | Phosphorus. Impurity, kept low for toughness and weld cracking resistance. |
| S | ≤ 0.030 | Sulfur. Impurity; low sulfur improves pitting resistance, hot workability and polishability. |
| Cr | 16.00 – 18.00 | Chromium. Forms the passive film; the main driver of corrosion and oxidation resistance. |
| Ni | 10.00 – 14.00 | Nickel. Stabilizes austenite, improves toughness and resistance to reducing acids. |
| Mo | 2.00 – 3.00 | Molybdenum. Raises pitting and crevice resistance in chlorides (×3.3 in PREN). |
| N | ≤ 0.10 | Nitrogen. Strengthens, stabilizes austenite and adds pitting resistance (×16 in PREN). |
| PREN (Cr + 3.3Mo + 16N) | 22.6 – 25.2 (minimum – mid-range) | Calculated from the limits above, not a requirement of GB/T 4237 |
Values are maximum unless a range is given. The mill reports the ladle (heat) analysis on the certificate; this is the figure to compare with Table 15.
Check analysis of 06Cr17Ni12Mo2 plate
A check analysis drilled from the finished plate may differ slightly from the heat analysis. GB/T 4237 refers to GB/T 222 for the permitted deviations; the table applies them to the 06Cr17Ni12Mo2 limits. Deviations apply to one side of a range only, never to both sides in the same heat.
| Element | Heat analysis limit (%) | Permitted deviation | Product analysis limit (%) |
|---|---|---|---|
| C | ≤ 0.08 | ±0.01 | ≤ 0.09 |
| Si | ≤ 0.75 | ±0.05 | ≤ 0.80 |
| Mn | ≤ 2.00 | ±0.04 | ≤ 2.04 |
| P | ≤ 0.045 | +0.010 | ≤ 0.055 |
| S | ≤ 0.030 | +0.005 | ≤ 0.035 |
| Cr | 16.00 – 18.00 | ±0.20 | 15.80 – 18.20 |
| Ni | 10.00 – 14.00 | ±0.10 (min) / ±0.15 (max) | 9.90 – 14.15 |
| Mo | 2.00 – 3.00 | ±0.10 | 1.90 – 3.10 |
| N | ≤ 0.10 | ±0.01 | ≤ 0.11 |
Where the table says ‘by agreement’, the deviation is not tabulated for that content level and should be agreed in the contract, usually by reference to ASTM A480 Table A1.1.
Mechanical properties of 06Cr17Ni12Mo2 plate
| Property | 06Cr17Ni12Mo2 (Table 20) |
|---|---|
| Proof strength Rp0.2, MPa | ≥ 205 |
| Tensile strength Rm, MPa | ≥ 515 |
| Elongation A, % | ≥ 40 |
| Hardness HBW | ≤ 217 |
| Hardness HRB | ≤ 95 |
| Hardness HV | ≤ 220 |
Values apply to plate in the delivery heat-treated condition, tested transversely per GB/T 228.1. Hardness is checked by one method chosen by the mill.
How 06Cr17Ni12Mo2 performs in corrosive service
Molybdenum raises resistance to chlorides, sulfurous media and reducing acids. The low-carbon and nitrogen variants keep that resistance across welds.
PREN of 06Cr17Ni12Mo2 from the GB/T 4237 limits: 22.6 – 25.2. PREN is a ranking tool for pitting in chlorides, not a guarantee; temperature, crevices, deposits and weld finish matter as much.
Intergranular corrosion: GB/T 4237-2015 Table 30 lists this grade for the copper–copper sulfate–sulfuric acid test (GB/T 4334 Method E) in the solution-treated condition. When the order calls for it, bent specimens must show no intergranular cracks.
If service is harsher than 06Cr17Ni12Mo2 can handle, the next step up in this batch is GB/T 4237 06Cr19Ni13Mo3 S31708.
Cross-reference to other standards
| Standard system | Equivalent / closest grade |
|---|---|
| China GB/T 4237-2015 | 06Cr17Ni12Mo2 (S31608) |
| Former Chinese name | 0Cr17Ni12Mo2 |
| ASTM A240/A240M | Type 316 / S31600 |
| EN 10088-2 | X5CrNiMo17-12-2 / 1.4401 |
| JIS G4304 (hot rolled) | SUS316 |
| Common name | 316 |
Equivalent grades are close in chemistry and properties but are never identical: limits on carbon, nitrogen and residual elements differ. For dual or multiple certification the heat must meet every standard named on the order, and we confirm that from the heat chemistry before quotation.
Related pages: ASTM A240 Type 316, ASME SA240 316, JIS G4305 SUS316, AISI 316. See also our ASTM A240/A240M and JIS G4305 plate lists.
Specification summary
| Item | GB/T 4237-2015 requirement / SHH STEEL supply |
|---|---|
| Standard | GB/T 4237-2015 Hot rolled stainless steel plate, sheet and strip (current edition, replaces GB/T 4237-2007) |
| Grade / unified code | 06Cr17Ni12Mo2 / S31608 |
| Steel class | Austenitic |
| Chemical composition | Table 15 (heat analysis); product analysis per GB/T 222 |
| Mechanical properties | Table 20 |
| Product forms | Hot-rolled thick plate (3.0 – 200 mm in the standard), hot-rolled wide strip and cut plate (2.0 – 25.4 mm) |
| Our usual thickness range | 3 – 120 mm (to 150 mm by mill order) |
| Delivery condition | ≥ 1 040 °C, water quench or other rapid cooling |
| Surface | Hot rolled, heat treated, pickled (No.1 / 1D) as standard; ground or polished by agreement |
| Density | 8.0 g/cm³ |
| Certificate | EN 10204 3.1 mill certificate; 3.2 with third-party inspection on request |
Sister grades on the same standard are listed under GB/T 4237; cold-rolled sheet of the same chemistry is ordered to GB/T 3280, and all our plate lines sit in stainless steel sheets and plates.
06Cr17Ni12Mo2 compared with related grades
The table compares 06Cr17Ni12Mo2 with the grades buyers most often weigh it against. Strength values are GB/T 4237-2015 minimums; PREN is calculated from the minimum chemistry.
| Grade (GB/T 4237) | Key chemistry, % | PREN min | Rp0.2 min, MPa | Rm min, MPa |
|---|---|---|---|---|
| 06Cr17Ni12Mo2 S31608 | C ≤ 0.08, Cr 16.00 – 18.00, Ni 10.00 – 14.00, Mo 2.00 – 3.00, N ≤ 0.10 | 22.6 | 205 | 515 |
| GB/T 4237 022Cr17Ni12Mo2 S31603 | C ≤ 0.030, Cr 16.00 – 18.00, Ni 10.00 – 14.00, Mo 2.00 – 3.00, N ≤ 0.10 | 22.6 | 180 | 485 |
| GB/T 4237 07Cr17Ni12Mo2 S31609 | C 0.04 – 0.10, Cr 16.00 – 18.00, Ni 10.00 – 14.00, Mo 2.00 – 3.00 | 22.6 | 205 | 515 |
| GB/T 4237 06Cr17Ni12Mo2Ti S31668 | C ≤ 0.08, Cr 16.00 – 18.00, Ni 10.00 – 14.00, Mo 2.00 – 3.00 | 22.6 | 205 | 515 |
| GB/T 4237 06Cr19Ni10 S30408 | C ≤ 0.07, Cr 17.50 – 19.50, Ni 8.00 – 10.50, N ≤ 0.10 | 17.5 | 205 | 515 |
| GB/T 4237 06Cr19Ni13Mo3 S31708 | C ≤ 0.08, Cr 18.00 – 20.00, Ni 11.00 – 15.00, Mo 3.00 – 4.00, N ≤ 0.10 | 27.9 | 205 | 515 |
316 still pits in warm seawater and in stagnant brine; for immersed seawater service look at 2205 or a 6Mo grade. For welded tanks the low-carbon 022Cr17Ni12Mo2 is the safer default, and most mills supply 316/316L dual-certified plate.
Welding and fabrication of 06Cr17Ni12Mo2
Use ER316L/E316L filler, or ER317L when the weld must not be the weak point in chloride service. A small ferrite number (FN 3–10) in the weld metal prevents hot cracking.
Interpass ≤150 °C, no preheat, clean back purge with argon for root passes. Pickle and passivate after welding: heat tint lowers pitting resistance more in Mo grades than the weld itself.
Cutting: we cut 06Cr17Ni12Mo2 by plasma (up to about 150 mm), laser (thin plate) or waterjet, and remove the heat-affected edge by machining where the drawing requires it.
Annealing / solution treatment
Recommended heat treatment for 06Cr17Ni12Mo2 (GB/T 4237-2015 Annex C): ≥ 1 040 °C, water quench or other rapid cooling.
Cool rapidly through 850–450 °C after annealing; slow cooling of thick Mo-bearing plate risks carbide and sigma precipitation.
Surface options and cut-to-size service
| Finish | Description | Availability for this grade |
|---|---|---|
| No.1 / 1D | Hot rolled, heat treated, pickled; the GB/T 4237 standard surface | Standard |
| Shot-blasted + pickled | Uniform matte for welded structures | On request |
| No.4 / brushed | Abrasive finish, grit 150–180 | Warehouse processing, thin plate |
| HL (hairline) | Long continuous lines, decorative | Warehouse processing, thin plate |
| 8K mirror | Polished reflective finish | Warehouse processing, limited sizes |
| 2B / BA | Cold-rolled finishes (ordered as GB/T 3280 sheet, not hot-rolled plate) | Sheet only |
Our warehouse cuts plate to size (plasma, laser, waterjet, saw), bevels weld edges, polishes and applies PVC protective film. Processed plate ships with the original mill heat number marked. Ask for cut pieces of other stainless steel products at the same time to consolidate freight.
Where this plate goes
Where buyers specify it:
- Chemical process vessels, reactors and storage tanks
- Marine fittings, coastal architecture and offshore topside parts
- Pulp and paper equipment
- Pharmaceutical and food plants using chloride cleaners
- Heat exchanger plates and tubesheets
- Flue gas and scrubber parts in mild conditions
Buyers specifying 06Cr17Ni12Mo2 for these jobs often compare it with GB/T 4237 022Cr17Ni12Mo2 S31603 and GB/T 4237 019Cr19Mo2NbTi S11972; the comparison table on this page shows the differences.
International grade pages for the alternatives mentioned above: ASTM A240 Type 316L, ASTM A240 Type 316H, ASTM A240 Type 316Ti, ASTM A240 Type 304.
Dimensions and plate weight
| Dimension | Typical supply |
|---|---|
| Thickness | 3 – 120 mm (to 150 mm by mill order) |
| Width | 1 000 / 1 219 / 1 250 / 1 500 / 1 800 / 2 000 mm; wider by mill order |
| Length | 2 000 / 2 438 / 3 000 / 6 000 mm or cut to size |
| Flatness | Per GB/T 4237; ≤15 mm per metre for plate up to 25 mm unless agreed tighter |
| Thickness tolerance | Per the GB/T 4237 dimensional tolerance tables (normal or higher accuracy as ordered) |
| Edge | Mill edge or cut edge |
Weight: plate mass in kg/m² = thickness (mm) × density (8.0 g/cm³). A 10 mm 06Cr17Ni12Mo2 plate weighs about 80.0 kg/m²; a 1 500 × 6 000 × 10 mm plate about 720 kg.
Inspection, tests and mill certificates
- Heat chemical analysis on every heat; product analysis by agreement
- Tensile test (Rp0.2, Rm, A) per batch
- Hardness test
- Intergranular corrosion test, GB/T 4334 Method E (Table 30)
- Ultrasonic testing (NB/T 47013.3 or ASTM A578) when specified
- Positive material identification (PMI) on every plate leaving our warehouse
- Visual and dimensional inspection; third-party inspection (SGS, BV, TÜV, Intertek) at the buyer’s request
Certificates follow EN 10204 3.1 as standard. Where plate is also certified to ASME SA240 or ASTM A240, both standards are shown on one certificate.
Supply chain and lead time
06Cr17Ni12Mo2 is a mainstream grade at Chinese stainless mills. We supply it from our own stock and processing warehouse, and by mill order from major producers such as TISCO and Baosteel Stainless, for which we act as a sales agent. Stock plate ships in about 1–2 weeks after cutting; mill orders typically take 30–60 days depending on thickness and rolling schedule.
Every plate is traceable to its heat number, and copies of the mill certificates stay on file for repeat orders and audits. The same mills also supply our ASTM A240, ASME SA240, JIS G4305 and AISI plate ranges, so mixed-standard orders can ship together.
What to put on a 06Cr17Ni12Mo2 purchase order
- Standard and edition: GB/T 4237-2015
- Grade and code: 06Cr17Ni12Mo2 (S31608); add the equivalent if dual certification is needed
- Thickness × width × length, quantity in pieces or tonnes
- Thickness tolerance class and flatness if tighter than standard
- Surface finish and protective film
- Tests beyond the standard (IGC, UT, impact, ferrite, PMI, grain size)
- Certificate type (EN 10204 3.1 / 3.2) and inspection body
- Marking, packing (wooden cases, steel pallets) and delivery terms
Send the list to SHH STEEL and we return a quotation with mill, lead time and stock options. Other grades from the same standard can be combined in one shipment; browse GB/T 4237 plate grades.
Working with SHH STEEL
- Mill-direct prices with our own export documentation
- Own processing warehouse: cutting, bevelling, polishing, PVC film
- PMI and dimensional check before packing
- Mixed-grade shipments across our AISI stainless and GB/T plate ranges
- Technical answers from people who read the standard, not just the price list
SHH STEEL has exported stainless and carbon steel plate to buyers in Asia, the Middle East, Africa, Europe and the Americas.
FAQ
- Is 06Cr17Ni12Mo2 the same as 316?
- Yes. 06Cr17Ni12Mo2 (S31608, old name 0Cr17Ni12Mo2) is GB/T 4237's 316: C ≤0.08%, Cr 16.00–18.00%, Ni 10.00–14.00%, Mo 2.00–3.00%. That matches ASTM A240 Type 316 (S31600), EN 1.4401 and JIS SUS316.
- What is the chemical composition of 06Cr17Ni12Mo2?
- Under GB/T 4237-2015 Table 15, 06Cr17Ni12Mo2 (S31608) has C ≤ 0.08, Cr 16.00 – 18.00, Ni 10.00 – 14.00, Mo 2.00 – 3.00, N ≤ 0.10. Phosphorus is limited to ≤0.045% and sulfur to ≤0.030%.
- What are the mechanical properties of 06Cr17Ni12Mo2 plate?
- GB/T 4237-2015 Table 20 requires for 06Cr17Ni12Mo2: proof strength Rp0.2 ≥205 MPa, tensile strength ≥515 MPa and elongation ≥40%, hardness ≤217 HBW. Values apply to plate in the delivery heat-treated condition.
- Is 06Cr17Ni12Mo2 stainless steel magnetic?
- Not in the annealed condition. 06Cr17Ni12Mo2 is austenitic, so annealed plate is essentially non-magnetic; cold work can induce slight magnetism, mostly at cut and bent edges.
- What thickness of 06Cr17Ni12Mo2 plate can you supply?
- Under GB/T 4237 we supply 06Cr17Ni12Mo2 hot-rolled plate in 3 – 120 mm (to 150 mm by mill order), widths up to 2 000 mm (wider by mill order), cut to size in our warehouse. Thinner material is cold-rolled sheet to GB/T 3280.
- What is the PREN of 06Cr17Ni12Mo2?
- Using PREN = Cr + 3.3Mo + 16N and the GB/T 4237-2015 limits, 06Cr17Ni12Mo2 has a PREN of about 22.6 at minimum chemistry and 25.2 at mid-range.
Conclusion
GB/T 4237 06Cr17Ni12Mo2 (S31608) is a molybdenum-bearing austenitic plate grade, known internationally as 316. It is defined by Table 15 chemistry (C ≤ 0.08, Cr 16.00 – 18.00, Ni 10.00 – 14.00, Mo 2.00 – 3.00, N ≤ 0.10) and Table 20 properties of at least 205 MPa proof strength and 515 MPa tensile strength. Typical uses include chemical process vessels, reactors and storage tanks, marine fittings, coastal architecture and offshore topside parts and pulp and paper equipment. 316 still pits in warm seawater and in stagnant brine; for immersed seawater service look at 2205 or a 6Mo grade.
Before ordering, state the standard edition, the grade name with its code, and any extra tests, so that the mill certificate matches your design documents. SHH STEEL supplies 06Cr17Ni12Mo2 plate from stock and by mill order, cut to size and finished in our own warehouse, with EN 10204 3.1 certificates. For related grades see GB/T 4237 022Cr17Ni12Mo2 S31603 and GB/T 4237 07Cr17Ni12Mo2 S31609, our GB/T 4237 category and the ASTM A240 Type 316 page. Send your sizes and quantities for a quotation.